Productos

ELECTRODO DE ACERO INOXIDABLE

  • Detalles
  • El mensaje

STAINLESS STEEL ELECTRODE

NOMBRE

ESTáNDAR

DIáMETRO(MM)

COMPOSICIóN QUíMICA DE METAL SOLDADO (%)

PROPIEDADES MECáNICAS DE WELD METAL

CARACTERíSTICAS Y APLICACIóN

SH-A002

AWS E308L-16

BS 19.9.LAR

DIN E19 9LR23

GB E308L-16

JIS D308L-16

2.0

2.5

3.2

4.0

5.0

C ≤0.04

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

S ≤0.030

P ≤0.040

TENSILE STRENGTH

≥ 520MPa

ELONGATION

≥35%


UN ELECTRODO AC / DC DE RECUBRIMIENTO DE CAL-TITANIA PARA SOLDADURA DE ACERO INOXIDABLE O ACERO ESTRUCTURAL DE BAJA CARBONO EXTRA BAJO TEMPERATURAS DE TRABAJO A CONTINUACIóN

300 ° C Y CORROSIóN.


 

 

SH-A022

AWS E316L-16

BS 19.12.3.LAR

DIN E1912 3LR23

GB E316L-16

JIS D316L-16

2.0

2.5

3.2

4.0

5.0

C ≤0.04

Mn 0.5-2.5

Si ≤0.90

Cr 17.0-20.0

Ni 11.0-14.0

Mo 2.0-2.5

TENSILE STRENGTH

≥490MPa

ELONGATION

≥ 30%


UN ELECTRODO AC / DC DE RECUBRIMIENTO CON LIMA-TITANIA CON UN CONTENIDO EXTRA BAJO DE CARBONO EN METAL SOLDADO. ESTá DISEÑADO PARA SOLDAR Cr Cr ACERO INOXIDABLE.

 

 

SH-A102

AWS E308-16

BS 19.9.AR

DIN E19 9R23

GB E308-16

JIS D308-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

S ≤0.030

P ≤0.040

TENSILE STRENGTH

≥550MPa

ELONGATION

≥ 35%


ELECTRODO ASTAINLESS CON RECUBRIMIENTO DE LIMITACIóN. ADECUADO PARA SOLDAR 0Cr19Ni9 O 0Cr18Ni11Ti ACERO INOXIDABLE SUJETO A TEMPERATURAS DE TRABAJO INFERIOR A 300 ° C Y CORROSIóN.

SH-A132

AWS E347-16

BS 19.9.Nb AR

DIN E19 9 Nb R23

GB E347-16

JIS D347-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 18.0-21.0

Ni 9.0-11.0

Nb 8 x C-1.00

TENSILE STRENGTH

≥520MPa

ELONGATION

≥ 25%


UN ELECTRODO AC / DC DE RECUBRIMIENTO CON LIMóN-TITANIA CON NIOBIUM COMO AGENTE ESTABILIZADOR. ES ADECUADO PARA SOLDAR TITANIO ESTABILIZADO 0Cr18Ni 11 Ti ACERO INOXIDABLE SUJETO A CORROSIóN.

SH-A202

AWS E316-16

BS 19.12.3.AR

DIN E19 12 3R23

GB E316-16

JIS D316-16

2.0

2.5

3.2

4.0

5.0

C ≤0.08

Mn 0.5-2.5

Si ≤0.90

Cr 17.0-20.0

Ni 11.0-14.0

Mo 2.0-3.0

TENSILE STRENGTH

≥520MPa

ELONGATION

≥ 30%


UNA CORRIENTE AC / DC DE REVESTIMIENTO DE LIMA-TITANIA. CONVENIENTE PARA LA SOLDADURA 0Cr18Ni12Mo2 ACERO INOXIDABLE O ESTRUCTURAS SOMETIDAS A áCIDO. TAMBIéN CONVENIENTE PARA SOLDAR LAS PLACAS DELGADAS.

 

SHA102

AWS E309-16

BS 23.12.AR

DIN E23 12R23

GB E309-16 JIS D309-16

2.0

2.5

3.2

4.0

5.0

C ≤0.15

Mn 0.5-2.5

Si ≤0.90

Cr 22.0-25.0

Ni 12.0-14.0

TENSILE STRENGTH

≥550MPa

ELONGATION

≥ 25%


ELECTRODO DE RECUBRIMIENTO DE ALIME-TITANIA PARA SOLDADURA DE ACERO INOXIDABLE, ACERO ALTO-ALTO Y ACERO ALTO-Mn. CONVENIENTE PARA UNIRSE DEL ACERO INOXIDABLE 308 AL ACERO LEVE.